德国 TOPASCOC 9903D-10 高纯度防潮高刚性耐化学食品包装

详细信息

	品牌：德国 TOPAS		加工级别：注塑级		用途级别：食品包装
	类型：标准料

TOPAS® 9903D-10

Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 9903D-10 is a very low glass transition temperature (T g =33°C) film extrusion grade. It is designed to deliver high shrinkage at low temperatures in shrink packaging applications. It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and general purpose applications. It is used in blends in monolayer products, and alone or in blends in multilayer films. It can be used in both cast and blown film processes. The leading film applications are shrink films and labels. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended. Due to the low glass transition temperature of this grade, shipment and storage of pellets at room temperature or below is strongly recommended.

Selected Applications

Shrink films and labels

Food packaging

Food contact

Leading Attributes

High shrink at low temperatures, low stress, toughness

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

TOPAS 9506F-500 - robust low temperature (T g =65°C) extrusion grade

TOPAS 9506F-04 - high clarity extrusion grade

物性信息：

基本信息
特性	纯度高防潮刚性，高共聚物耐化学性良好韧性良好食品接触的合规性收缩性高通用无 BPA 无定形的无卤中等透明度
用途	包装薄膜标签多层薄膜混合流延薄膜食品包装通用
机构评级	FDA FCN 405 欧洲 10/1/2011 12:00:00 AM
形式	粒子
加工方法	薄膜挤出吹塑薄膜流延薄膜热成型

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm³	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	0.90	g/10 min	ISO 1133
230°C/2.16 kg	3.7	g/10 min	ISO 1133
260°C/2.16 kg	7.4	g/10 min	ISO 1133
溶化体积流率（MVR）			ISO 1133
190°C/2.16 kg	1.00	cm³/10min	ISO 1133
230°C/2.16 kg	4.00	cm³/10min	ISO 1133
260°C/2.16 kg	8.00	cm³/10min	ISO 1133
吸水率 (饱和, 23°C)	0.010	%	ISO 62

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	100	µm
拉伸模量 (100 µm, 铸造薄膜)	1260	MPa	ISO 527-3/1
拉伸应力			ISO 527-3/50
MD : 断裂, 100 µm, 铸造薄膜	25.0	MPa	ISO 527-3/50
TD : 断裂, 100 µm, 铸造薄膜	22.0	MPa	ISO 527-3/50
伸长率			ISO 527-3/50
MD : 断裂, 100 µm, 铸造薄膜	> 150	%	ISO 527-3/50
TD : 断裂, 100 µm, 铸造薄膜	> 100	%	ISO 527-3/50
透氧率 (23°C, 100 µm, 挤塑薄膜, 50% RH)	39	cm³·mm/m²/atm/24 hr	ASTM D3985
水气透过率 (100 µm, 23°C, Cast Film, 85% RH)	0.19	g·mm/m²/atm/24 hr	ASTM F1249

热性能	额定值	单位制	测试方法
玻璃转化温度	33.0	°C	ISO 11357-2

光学性能	额定值	单位制	测试方法
光泽度 (60°, 100 µm, 铸造薄膜)	> 100		ISO 2813
雾度 (100 µm, 铸造薄膜)	< 1.0	%	ISO 14782

挤出	额定值	单位制
挤塑机进料部分	20 到 60	°C
挤出机螺杆长径比L / D	> 28:1
料筒1区温度	210 到 220	°C
料筒2区温度	230 到 240	°C
料筒3区温度	230 到 240	°C
料筒4区温度	230 到 240	°C
口模温度	230 到 240	°C

挤压说明
Head Pressure: P >140 bar / 2000 psi; Fine screen packs as neededScrew Speed: RPM > 50% nominalScrew Design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 inch

留言

*详细需求：	德国 TOPASCOC 9903D-10 高纯度防潮高刚性耐化学食品包装
*手机：
联系人：
电话：
E-mail：
公司：
	已经阅读并同意《谷瀑服务条款》《隐私政策》允许谷瀑将询价单分发给更多优质供应商

供应商的其他相关信息
查看更多
美国杜邦 TPEE 4056 抗

美国杜邦 TPEE 6356 高

美国杜邦 TPEE 6356 高

美国杜邦TPEE 4556 抗

美国杜邦TPEE 8238 耐

产品搜索
产品分类
留言

文国祥

在线联系

手机：13929209907

您输入的内容请介于 5 到 2000 字之间

请输入正确手机号

同意《谷瀑服务条款》《隐私政策》

允许谷瀑将询价单分发给更多优质供应商
公司相册

东莞市领汉时代新材料有限公司

东莞市领汉时代新材料有限公司主要经营：PA12.PEI.PPS.PA66,,PC,无卤阻燃.耐寒PC,阻燃ABS,HTN高温尼龙.导热塑料 耐磨塑料 基础创新特殊塑料。

德国 TOPASCOC 9903D-10 高纯度 防潮 高刚性 耐化学 食品包装

店内推荐产品

详细信息

TOPAS® 9903D-10

留言

供应商的其他相关信息

产品搜索

产品分类

留 言

公司相册

东莞市领汉时代新材料有限公司主要经营：PA12.PEI.PPS.PA66,,PC,无卤阻燃.耐寒PC,阻燃ABS,HTN高温尼龙.导热塑料耐磨塑料基础创新特殊塑料。

德国 TOPASCOC 9903D-10 高纯度防潮高刚性耐化学食品包装

留言