    TOPAS® 5013F-04

    Cyclic Olefin Copolymer
    Topas Advanced Polymers, Inc.
    产品说明:
    Product Description
    TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.

    Selected Applications
    • Decorative film and sheet
    • General packaging
    • Food packaging
    • Blown film
    • Healthcare and food contact

    Leading Attributes
    • Gloss, hardness, chemical resistance, forming
    • Easy or linear tear, heat resistance, hot fill, gloss
    • Not manufactured with BPA, phthalates, or halogens
    • High strength and high productivity
    • Broad regulatory compliance

    Related Grades for Packaging and Film Extrusion
    • TOPAS 6013F-04 - high temperature grade with standard flow

    物性信息:
    基本信息  
    特性
    • 纯度高
    • 防潮
    • 刚性,高
    • 高光
    • 高强度
    • 共聚物
    • 流动性高
    • 耐化学性良好
    • 清晰度,高
    • 食品接触的合规性
    • 无 BPA
    • 无定形的
    • 无卤
    用途
    • 包装
    • 薄膜
    • 混合
    • 片材
    • 食品包装
    • 医疗/护理用品
    机构评级
    • FDA FCN 405
    • 欧洲 10/1/2011 12:00:00 AM
    形式
    • 粒子
    加工方法
    • 薄膜挤出
    • 吹塑薄膜
    • 共挤薄膜
    • 流延薄膜
    • 热成型
    物理性能 额定值 单位制 测试方法
    密度 1.02 g/cm³ ISO 1183
    熔流率(熔体流动速率)     ISO 1133
        190°C/2.16 kg < 0.10 g/10 min ISO 1133
        230°C/2.16 kg 8.0 g/10 min ISO 1133
    溶化体积流率(MVR)     ISO 1133
        190°C/2.16 kg < 0.100 cm³/10min ISO 1133
        230°C/2.16 kg 9.00 cm³/10min ISO 1133
    吸水率 (饱和, 23°C) 0.010 % ISO 62
    薄膜 额定值 单位制 测试方法
    薄膜厚度 - 经测试 70 µm  
    拉伸模量     ISO 527-3/1
        MD : 70 µm, 铸造薄膜 2600 MPa ISO 527-3/1
        TD : 70 µm, 铸造薄膜 2500 MPa ISO 527-3/1
    拉伸应力     ISO 527-3/50
        MD : 断裂, 70 µm, 铸造薄膜 35.0 MPa ISO 527-3/50
        TD : 断裂, 70 µm, 铸造薄膜 25.0 MPa ISO 527-3/50
    伸长率     ISO 527-3/50
        MD : 断裂, 70 µm, 铸造薄膜 1.4 % ISO 527-3/50
        TD : 断裂, 70 µm, 铸造薄膜 1.1 % ISO 527-3/50
    落锤冲击 (70 µm, 铸造薄膜) < 36 g ISO 7765-1
    埃尔曼多夫抗撕强度     ISO 6383-2
        MD : 70 µm, 铸造薄膜 0.11 N ISO 6383-2
        TD : 70 µm, 铸造薄膜 0.11 N ISO 6383-2
    透氧率 (23°C, 70 µm, 挤塑薄膜, 50% RH) 26 cm³·mm/m²/atm/24 hr ASTM D3985
    水气透过率 (70 µm, 38°C, Cast Film, 90% RH) 0.14 g·mm/m²/atm/24 hr ASTM F1249
    热性能 额定值 单位制 测试方法
    玻璃转化温度 134 °C ISO 11357-2
    光学性能 额定值 单位制 测试方法
    光泽度 (60°, 70.0 µm, 铸造薄膜) > 100   ISO 2813
    雾度 (70.0 µm, 铸造薄膜) < 1.0 % ISO 14782
    挤出 额定值 单位制  
    挤塑机进料部分 20 到 70 °C  
    挤出机螺杆长径比L / D > 28:1    
    料筒1区温度 220 到 240 °C  
    料筒2区温度 220 到 240 °C  
    料筒3区温度 220 到 240 °C  
    料筒4区温度 220 到 240 °C  
    口模温度 220 到 240 °C  
    挤压说明
    Head pressure: P > 140 bar / 2000 psi; Fine screen packs as neededScrew Speed: RPM > 50% nominalScrew design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 in Grooved Feed: Hot temperature: 120°C (212°F)
  • 留言

    *详细需求:
    *手  机:
    联 系 人:
    电    话:
    E-mail:
    公  司:
    谷瀑服务条款》《隐私政策
东莞市领汉时代新材料有限公司 电话:0769-87781190 手机:13929209907 地址: 东莞市樟木头南方商业大楼312室
内容声明:谷瀑为第三方平台及互联网信息服务提供者,谷瀑(含网站、客户端等)所展示的商品/服务的标题、价格、详情等信息内容系由店铺经营者发布,其真实性、准确性和合法性均由店铺经营者负责。谷瀑提醒您购买商品/服务前注意谨慎核实,如您对商品/服务的标题、价格、详情等任何信息有任何疑问的,请在购买前通过谷瀑与店铺经营者沟通确认;谷瀑上存在海量店铺,如您发现店铺内有任何违法/侵权信息,请在谷瀑首页底栏投诉通道进行投诉。