Chevron Phillips Xtel® XK2040 Polyphenylene Sulfide Alloy

Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced
Chevron Phillips Chemical Company LP
产品说明：
Natural Color Polyphenylene Sulfide Alloy

 

Xtel™ XK2040 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength and electrical properties along with excellent flow in thin-walled parts, low flash characteristics, and fast cycle times. Xtel™ XK2040 can be easily molded in conventional injection molding equipment utilizing water heated molds.

Comments: Test specimen molding conditions: Stock Temperature, 280-305°C; Mold Temperature, 80°C; ASTM Values Converted to SI Units

Data provided by Chevron Phillips Chemical Company LP.

 

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.70 g/cc	0.0614 lb/in³	ASTM D792
吸水率	0.090 %	0.090 %	ASTM D570
线性成型收缩率	0.0030 cm/cm	0.0030 in/in	102 mm X 102 mm X 3.2 mm Plaques, Edge Gated
线性成型收缩率，横向	0.0050 cm/cm	0.0050 in/in	Measured on 102 mm X 102 mm X 3.2 mm Plaques, Edge Gated

机械性能	额定值 (公制)	额定值 (英制)	测试方法
极限抗拉强度	170 MPa	24700 psi	ASTM D638
伸长率 (断裂)	1.4 %	1.4 %	ASTM D638
弯曲强度	240 MPa	34800 psi	ASTM D790
弯曲模量	13.0 GPa	1890 ksi	ASTM D790
压缩屈服强度	205 MPa	29700 psi	ASTM D695
悬壁梁缺口冲击强度	0.850 J/cm	1.59 ft-lb/in	ASTM D256
悬壁梁无缺口冲击强度	5.10 J/cm	9.55 ft-lb/in	ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电常数	3.8 @Frequency 1e+6 Hz	3.8 @Frequency 1e+6 Hz	ASTM D150
	4.0 @Frequency 1000 Hz	4.0 @Frequency 1000 Hz	ASTM D150
介电强度	22.0 kV/mm	559 kV/in	ASTM D149
耗散因数	0.0090 @Frequency 1000 Hz	0.0090 @Frequency 1000 Hz	ASTM D150
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz	ASTM D150
耐电弧性	100 sec	100 sec	ASTM D495
相比耐漏电起痕指数(CTI)	250 V	250 V	UL 746A

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	18.0 µm/m-°C @Temperature 100 - 200 °C	10.0 µin/in-°F @Temperature 212 - 392 °F	Axial; ASTM E831
	18.0 µm/m-°C @Temperature -50.0 - 50.0 °C	10.0 µin/in-°F @Temperature -58.0 - 122 °F	Axial; ASTM E831
线性热膨胀系数,横向流动	50.0 µm/m-°C @Temperature 20.0 °C	27.8 µin/in-°F @Temperature 68.0 °F	ASTM E831
	92.0 µm/m-°C @Temperature 100 - 200 °C	51.1 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
载荷下热变形温度(1.8 MPa)	250 °C	482 °F	ASTM D648
可燃性(UL94)	V-0	V-0

Chevron Phillips Xtel® XK2140 Polyphenylene Sulfide Alloy

Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced
Chevron Phillips Chemical Company LP
产品说明：
Black Polyphenylene Sulfide Alloy

 

Xtel™ XK2140 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength and electrical properties along with excellent flow in thin-walled parts, low flash characteristics, and fast cycle times. Xtel™ XK2140 can be easily molded in conventional injection molding equipment utilizing water heated molds.

Comments: Test specimen molding conditions: Stock Temperature, 280-305°C; Mold Temperature, 80°C; ASTM Values Converted to SI Units

Data provided by Chevron Phillips Chemical Company LP.

 

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.70 g/cc	0.0614 lb/in³	ASTM D792
吸水率	0.090 %	0.090 %	ASTM D570
线性成型收缩率	0.0030 cm/cm	0.0030 in/in	102 mm X 102 mm X 3.2 mm Plaques, Edge Gated
线性成型收缩率，横向	0.0050 cm/cm	0.0050 in/in	Measured on 102 mm X 102 mm X 3.2 mm Plaques, Edge Gated

机械性能	额定值 (公制)	额定值 (英制)	测试方法
极限抗拉强度	165 MPa	23900 psi	ASTM D638
伸长率 (断裂)	1.4 %	1.4 %	ASTM D638
弯曲强度	205 MPa	29700 psi	ASTM D790
弯曲模量	13.0 GPa	1890 ksi	ASTM D790
压缩屈服强度	195 MPa	28300 psi	ASTM D695
悬壁梁缺口冲击强度	0.800 J/cm	1.50 ft-lb/in	ASTM D256
悬壁梁无缺口冲击强度	4.30 J/cm	8.06 ft-lb/in	ASTM D256

电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电常数	3.8 @Frequency 1e+6 Hz	3.8 @Frequency 1e+6 Hz	ASTM D150
	4.0 @Frequency 1000 Hz	4.0 @Frequency 1000 Hz	ASTM D150
介电强度	22.0 kV/mm	559 kV/in	ASTM D149
耗散因数	0.0090 @Frequency 1000 Hz	0.0090 @Frequency 1000 Hz	ASTM D150
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz	ASTM D150
耐电弧性	100 sec	100 sec	ASTM D495
相比耐漏电起痕指数(CTI)	175 V	175 V	UL 746A

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	18.0 µm/m-°C @Temperature 100 - 200 °C	10.0 µin/in-°F @Temperature 212 - 392 °F	Axial; ASTM E831
	18.0 µm/m-°C @Temperature -50.0 - 50.0 °C	10.0 µin/in-°F @Temperature -58.0 - 122 °F	Axial; ASTM E831
线性热膨胀系数,横向流动	50.0 µm/m-°C @Temperature 20.0 °C	27.8 µin/in-°F @Temperature 68.0 °F	ASTM E831
	92.0 µm/m-°C @Temperature 100 - 200 °C	51.1 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
载荷下热变形温度(1.8 MPa)	250 °C	482 °F	ASTM D648
可燃性(UL94)	V-0	V-0

PPS的特性如下：
1、耐化学性能好。
2、蠕变量低。
3、吸水率低。
4、尺寸稳定性好。
5、弹性模量高。
6、阻燃。
聚苯硫醚（PPS）与聚醚醚酮（PEEK），聚砜（PSF），聚酰亚胺（PI），聚芳酯（PAR），液晶聚合物（LCP）一起被称为6大特种工程塑料。
PPS的突出性能：良好的耐热性能，热变形温度一般大于260℃，可在180~220℃温度范围使用，PPS是工程塑料中耐热性*好的品种之一；耐腐蚀性接近四氟乙烯，抗化学性仅次于聚四氟乙烯；电性能优异；机械性能优异；阻燃性能好。
PPS不足之处：价格太高，在耐高温材料中属底价，但比通用工程塑料高许多；韧性差，性脆；中粘度不稳定。
纯PPS因性能脆而很少使用，应用的PPS多为其改性能品种。具体有；40%玻璃纤维增强PPS（R-4），无机填充PPS（R-8），碳纤维增强PPS（G-6）等。PPS的发展和快，预计它将成为第六大工程材料。
（1）一般性能：PPS为一种外观白色，高结晶度、硬而脆的聚合物，纯PPS的相对密度为1.3，但改性后会增大。PPS吸水率极小，一般只有0.03%左右。PPS的阻燃性好，其氧指数高达44%以上，与其他塑料相比，它在塑料中属于高阻燃材料（纯PVA的氧指数为47%，PSF为30%，PA66为29%，MPPO为28%，PC为25%)。
（2）机械性能：纯PPS的机械性能不高，尤其冲击强度低。以玻璃纤维增强后会大幅度提高冲击强度，有27J/m，增大到76J/m，增大3倍；拉伸强度由6Mpa增大到 137Mpa，增大1倍。PPS的刚性很高。在工程材料少见。纯PPS的弯曲模量可达到3.8Gpa，无机填充改性后可到到12.6Gpa，增大5倍之多。而以刚性著称的PPO仅为2.55Gpa，PC仅为2.1Gpa。PPS在负荷下的耐蠕变性好；硬度高；耐磨性高，其1000转时的模量仅为0.04g，填充F4及二硫化钼后还会进一步得到改善；PPS还具有一定的自润性。PPS的机械性能对温度的敏感性能小。
（3）热学性能：PPS又有优异的热性能，短期可耐260℃，并可在200~240℃下长期使用；其耐性与PI相当，仅次于F4塑料，这是在热固性塑料中也不多见。
（4）电学性能：PPS的电性能十分突出，与其它工程材料相比，其介电常数与介电耗损角成切值都比较低，并且在较大的频率、温度及温度范围内变化不大；PPS的耐电弧好，可与热固性塑料媲美。PPS常用于电器绝缘材料，这在热固性材料中也不多见；其用量占30%左右。
（5）环境性能：PPS*大的特点之一为耐化学腐蚀性好，其化学稳定性仅次于F4：
PPS对大多酸。酯、铜、酚、及脂肪经、芳香经、氯代经等稳定，不耐氯代联苯及氧化性酸、氧化剂、浓硫酸、浓硝酸、王水、过氧化氢及次氯酸钠等。PPS耐辐射性好。