SABIC Innovative Plastics Lexan® 1173X PC Copolymer (Europe-Africa-Middle East)

Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Lexan* 1173X polycarbonate (PC) resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-30 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. Lexan 1173X resin is a general purpose product available in a wide range of opaque colors and may be an excellent candidate for a broad range of applications.

 

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.18 g/cc	1.18 g/cc	ASTM D792
密度	1.19 g/cc	0.0430 lb/in³	ISO 1183
水分吸收	0.150 %	0.150 %	23°C / 50% RH; ISO 62
饱和吸水率	0.35 %	0.35 %	ISO 62
线性成型收缩率,Flow	0.0040 - 0.0080 cm/cm @Thickness 3.20 mm	0.0040 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
线性成型收缩率，横向	0.0040 - 0.0080 cm/cm @Thickness 3.20 mm	0.0040 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
熔体流动速率	17 g/10 min @Load 1.20 kg, Temperature 300 °C	17 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
化合物熔体指数	16 g/10 min @Load 1.20 kg, Temperature 300 °C	16 g/10 min @Load 2.65 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
抗张强度(断裂)	55.0 MPa	7980 psi	50 mm/min; ISO 527
抗张强度(屈服)	57.0 MPa	8270 psi	50 mm/min; ISO 527
伸长率 (断裂)	100 %	100 %	50 mm/min; ISO 527
屈服伸长率	5.0 %	5.0 %	50 mm/min; ISO 527
拉伸模量	2.15 GPa	312 ksi	1 mm/min; ISO 527
弯曲强度	85.0 MPa	12300 psi	2 mm/min; ISO 178
弯曲模量	2.25 GPa	326 ksi	2 mm/min; ISO 178
悬壁梁缺口冲击强度	65.0 kJ/m²	30.9 ft-lb/in²	80*10*3; ISO 180/1A
	50.0 kJ/m² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	80*10*3; ISO 180/1A
	60.0 kJ/m² @Temperature 0.000 °C	28.6 ft-lb/in² @Temperature 32.0 °F	80*10*3; ISO 180/1A
悬壁梁无缺口冲击强度	NB	NB	80*10*3; ISO 180/1U
	NB @Temperature 0.000 °C	NB @Temperature 32.0 °F	80*10*3; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80*10*3; ISO 180/1U
简支梁无缺口冲击强度	NB	NB	Edgew 80*10*3 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eU
简支梁缺口冲击强度	6.50 J/cm²	30.9 ft-lb/in²	Edgew 80*10*3 sp=62mm; ISO 179/1eA
	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	Edgew 80*10*3 sp=62mm; ISO 179/1eA

热性能	额定值 (公制)	额定值 (英制)	测试方法
线形热膨胀系数 - 流动	75.0 µm/m-°C @Temperature 23.0 - 80.0 °C	41.7 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
线性热膨胀系数,横向流动	75.0 µm/m-°C @Temperature 23.0 - 80.0 °C	41.7 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
载荷下热变形温度(0.46 MPa)	136 °C	277 °F	edgew. Annealed 80°C, 4 hrs; ISO 75/Be
	137 °C @Thickness 3.20 mm	279 °F @Thickness 0.126 in	unannealed; ASTM D648
载荷下热变形温度(1.8 MPa)	125 °C	257 °F	Edgew 120*10*4 sp=100mm; ISO 75/Ae
	124 °C @Thickness 3.20 mm	255 °F @Thickness 0.126 in	unannealed; ASTM D648
维卡软化温度	144 °C	291 °F	Rate B/50; ASTM D1525
	144 °C	291 °F	Rate B/50; ISO 306
	145 °C	293 °F	Rate B/120; ISO 306
极限氧指数	32 %	32 %	ISO 4589
灼热丝试验	875 °C	1610 °F	IEC 60695-2-13
	875 °C	1610 °F	IEC 60695-2-13
	850 °C @Thickness 1.00 mm	1560 °F @Thickness 0.0394 in	IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	IEC 60695-2-12

材料描述		测试方法
球压试验，125°C+/-2℃	PASSES	IEC 60695-10-2

长期供应PC塑料原料，货源稳定， ，当天发货

供应德国拜耳PC 2405低粘度 热稳定 耐冲击 无色 易脱模供应德国拜耳

PC 2407低粘度 紫外线外及热稳定供应德国拜耳

PC 2458食品级 非增强通用品级供应德国拜耳

PC 2605中低粘度 注塑式挤塑成型 耐冲击 易脱模供应德国拜耳

PC 2805中粘度度 注塑式挤塑成型 热稳供应德国拜耳

PC 2807中粘度 紫外线外及热稳定供应德国拜耳

PC 2858食品级 防火V2中粘度供应德国拜耳

PC 2865中粘度 防火V0/6.0供应德国拜耳

PC 3208食品级 挤塑成型 耐冲击 水触稳定供应德国拜耳

PC 6485中粘度供应德国拜耳

PC 6555防火V0中高粘度 注塑式挤塑供应德国拜耳

PC 6557防火V0中粘度 易脱模供应德国拜耳

PC 9415玻璃纤维增强10%防火V2供应

PC德国拜耳1803供应

PC德国拜耳1095透明，

供应PC德国拜耳1800透明，

供应PC德国拜耳KU1-9531 185度

供应美国GE PC 101R-116高粘度

供应美国GE PC 121R-116易脱模 低粘度 高流动

供应美国GE PC 123R-116 UV稳定 低粘度 高流动

供应美国GE PC 124R-116食品级 低粘度 高流动

供应美国GE PC 141R-116易脱模 中粘度

供应美国GE PC 143R-116 UV稳定 中粘度

供应美国GE PC 144R-116食品级 中粘度

供应美国GE PC HF1110高流动性改良

供应美国GE PC SP7602玻璃纤维增强10% 流动 防火V0

供应美国GE PC SP7604玻璃纤维增强20% 流动 防火V0

供应美国GE PC HF1130 流动 紫外线尺寸稳定 耐热

供应美国GE PC 940 945防火V0不透明

供应美国GE PC 940A-116防火V0透明 中粘度

供应美国GE PC 943A-116防火V0透明 中粘度 耐候性改良

供应美国GE PC 945A-116防火V0透明

供应美国GE PC 953A-116防火V0不透明 紫外稳定 高粘度

供应美国GE PC 503R玻璃纤维增强10%防火V0紫外线稳定

供应美国GE PC 500R玻璃纤维增强10%防火V0易脱模

供应美国GE PC 3412R玻璃纤维增强20%防火V1易脱模

供应美国GE PC 3414R玻璃纤维增强40%防火V1易脱模

供应美国GE PC 3413R玻璃纤维增强30%防火V1易脱模

供应美国GE PC EXL1414超韧耐低温

供应美国GE PC EXL9330防火V0超韧耐低温

供应美国GE PC ML3403实心板材 紫外线稳定

供应美国GE PC ML3324中空阳光板 紫外线稳定

供应日本帝人PC L-1225L低粘度 用于超薄壁型电器、电子元件

供应日本帝人PC L-1225Z

供应日本帝人PC L-1250Y 光扩散PC适宜于采用注坯吹塑成型

供应日本帝人PC L-1250Z

供应日本帝人PC LN-2250Y防火V0

供应日本帝人PC AD-5503光学级

供应PC日本出光LC1700导光板

供应PC日本出光LC1500导光板

供应PC日本出光URZ2501光反射级 背光板

供应PC日本出光URZ2502光反射级 背光板

供应PC日本出光IR2200低粘度 易流动FDA认可 适合大型成型或薄膜制品

供应台湾奇美PC PC-110 V2中粘度10

供应台湾奇美PC PC-110U V2中粘度 耐候级10

供应台湾奇美PC PC-115 V2低黏度15

供应台湾奇美PC PC-122 V2高流动22

供应台湾奇美PC PC-122U V2高流动 耐候级22

供应日本三菱PC S3000UR易脱模

供应日本三菱PC S3001R食品级 中粘度

供应日本三菱PC S2001R食品级 中粘度

供应日本三菱PC S-3000VR耐候性改良 低粘度

供应日本三菱PC S-2000VR耐候性改良 中粘度

供应日本三菱PC FPR3500防火V0

供应日本三菱PC HPR3500光反射级 背光板

供应日本三菱PC GS2020MR2防火V0玻璃纤维20%增强

供应日本三菱PC GS2010MPH高抗冲击