• 基础创新塑料美国 PC/PET X7200 抗UV 高流动 耐高温 阻燃

    详细信息

     厂家:基础创新塑料美国  加工级别:挤出  特性:共混;阻燃;抗紫外;耐高温  
     是否环保:是  颜色:本色  用途:专用粒料  
     品牌: 基础创新塑料美国  型号:X7200   

    SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Asia Pacific)

    Polycarbonate/PET Polyester Blend
    SABIC Innovative Plastics (GE Plastics)
    产品说明:
    General purpose, UV stabilised Xylex grade

    This data was supplied by SABIC-IP for the Asia Pacific region.


    物性信息:
    物理性能 额定值 (公制) 额定值 (英制) 测试方法
    比重 1.20 g/cc 1.20 g/cc ASTM D 792
    密度 1.18 g/cc 0.0426 lb/in³ ISO 1183
    线性成型收缩率,Flow 0.0050 - 0.0070 cm/cm
    @Thickness 3.20 mm
    0.0050 - 0.0070 in/in
    @Thickness 0.126 in
    SABIC Method
    线性成型收缩率,横向 0.0050 - 0.0070 cm/cm
    @Thickness 3.20 mm
    0.0050 - 0.0070 in/in
    @Thickness 0.126 in
    SABIC Method
    熔体流动速率 12 g/10 min
    @Load 2.16 kg, Temperature 265 °C
    12 g/10 min
    @Load 4.76 lb, Temperature 509 °F
    ASTM D 1238
      12 g/10 min
    @Load 2.16 kg, Temperature 265 °C
    12 g/10 min
    @Load 4.76 lb, Temperature 509 °F
    [cm^3/10 min] Melt Volume Rate; ISO 1133
    机械性能 额定值 (公制) 额定值 (英制) 测试方法
    肖氏硬度 (邵氏 D) 75 75 10S reading; ASTM D 2240
    抗张强度(断裂) 56.0 MPa 8120 psi Type I, 50 mm/min; ASTM D 638
      56.0 MPa 8120 psi 50 mm/min; ISO 527
    抗张强度(屈服) 55.0 MPa 7980 psi Type I, 50 mm/min; ASTM D 638
      55.0 MPa 7980 psi 50 mm/min; ISO 527
    伸长率 (断裂) 135 % 135 % Type I, 50 mm/min; ASTM D 638
      >= 150 % >= 150 % 50 mm/min; ISO 527
    屈服伸长率 5.0 % 5.0 % Type I, 50 mm/min; ASTM D 638
      5.0 % 5.0 % 5 mm/min; ISO 527
    拉伸模量 1.88 GPa 273 ksi 50 mm/min; ASTM D 638
      2.00 GPa 290 ksi 1 mm/min; ISO 527
    弯曲强度 75.0 MPa 10900 psi 2 mm/min; ISO 178
      84.0 MPa 12200 psi 1.3 mm/min, 50 mm span; ASTM D 790
    弯曲模量 1.96 GPa 284 ksi 1.3 mm/min, 50 mm span; ASTM D 790
      2.00 GPa 290 ksi 2 mm/min; ISO 178
    悬壁梁缺口冲击强度 9.00 J/cm
    @Temperature 23.0 °C
    16.9 ft-lb/in
    @Temperature 73.4 °F
    ASTM D 256
      5.00 kJ/m²
    @Temperature -10.0 °C
    2.38 ft-lb/in²
    @Temperature 14.0 °F
    80*10*4; ISO 180/1A
      8.00 kJ/m²
    @Temperature 23.0 °C
    3.81 ft-lb/in²
    @Temperature 73.4 °F
    80*10*4; ISO 180/1A
    冲击试验 95.0 J
    @Temperature 23.0 °C
    70.1 ft-lb
    @Temperature 73.4 °F
    Instrumented Impact Total Energy; ASTM D 3763
    电气性能 额定值 (公制) 额定值 (英制) 测试方法
    体积电阻率 >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm ASTM D 257
    表面电阻 >= 1.00e+15 ohm >= 1.00e+15 ohm ASTM D 257
    相比耐漏电起痕指数(CTI) >= 600 V >= 600 V PLC code 0; UL 746A
    热性能 额定值 (公制) 额定值 (英制) 测试方法
    线形热膨胀系数 - 流动 80.0 µm/m-°C
    @Temperature 23.0 - 60.0 °C
    44.4 µin/in-°F
    @Temperature 73.4 - 140 °F
    ISO 11359-2
      105 µm/m-°C
    @Temperature -40.0 - 40.0 °C
    58.3 µin/in-°F
    @Temperature -40.0 - 104 °F
    ASTM E 831
    线性热膨胀系数,横向流动 80.0 µm/m-°C
    @Temperature 23.0 - 60.0 °C
    44.4 µin/in-°F
    @Temperature 73.4 - 140 °F
    ISO 11359-2
      105 µm/m-°C
    @Temperature -40.0 - 40.0 °C
    58.3 µin/in-°F
    @Temperature -40.0 - 104 °F
    ASTM E 831
    导热系数 0.230 W/m-K 1.60 BTU-in/hr-ft²-°F ISO 8302
    Hot Ball Pressure Test <= 105 °C <= 221 °F IEC 60695-10-2
    载荷下热变形温度(0.46 MPa) 96.0 °C
    @Thickness 3.20 mm
    205 °F
    @Thickness 0.126 in
    unannealed; ASTM D 648
    载荷下热变形温度(1.8 MPa) 99.0 °C 210 °F Edgew 120*10*4 sp=100mm; ISO 75/Ae
      90.0 °C
    @Thickness 3.20 mm
    194 °F
    @Thickness 0.126 in
    unannealed; ASTM D 648
    维卡软化温度 115 °C 239 °F Rate B/50; ASTM D 1525
      115 °C 239 °F Rate B/120; ISO 306
    可燃性(UL94) V-2
    @Thickness 3.00 mm
    V-2
    @Thickness 0.118 in
    UL 94
    灼热丝试验 750 °C
    @Thickness 1.00 mm
    1380 °F
    @Thickness 0.0394 in
    Glow Wire Flammability Index; IEC 60695-2-12
    光学性能 额定值 (公制) 额定值 (英制) 测试方法
    折射率 1.557 1.557 ISO 489
    雾度 1.1 %
    @Thickness 2.54 mm
    1.1 %
    @Thickness 0.100 in
    ASTM D 1003
    Transmission, Visible 88 %
    @Thickness 2.54 mm
    88 %
    @Thickness 0.100 in
    ASTM D 1003

    PC/PET合金材料介绍
    PC/PET合金材料由PC(聚碳酸酷)和PET(聚对苯二甲酸乙二酷)共混造料聚合而成。通常以共混造料后,以粒料形状供应。如果只把两种料简单的混合后,直接注塑,效果很差,会出现分层现象。
    PC 全名是聚碳酸醋,是分子链中含有碳酸酷基的高分子聚合物,根据酷基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。PC 的优点是室温刚而韧但高温的情况下,热变形严重。缺点是应力开裂,粘度大,易粘模。
    PET树脂英文名称:Polybutylene Terephthalate Resin。它由(DMT)进行酷交换或与精对苯二甲由1.4丁二醇与对苯二甲酸二甲酷酸(PTA)直接酷化后再经缩聚制得。其分子式为:(-C12H804-)nPET树脂为结晶形,熔点225C左右,相对密度 1.32:具有优良的力学性能,有自润滑性和耐磨性,摩擦系数低,耐热、耐候好:但缺口敏感性大:尺寸稳定性好,电性能优良,耐电弧性好:抗化学性及其优异,与醇、醚、脂肪烃、酸和盐的水溶液等不起作用,但不耐强酸和强藏。耐四氯化碳,在二氯乙烷中溶胀,在芳烃、乙酸中有些溶胀。
    PC/PET合金艰巨了两款材料的优点,具有良好的硬度和耐冲击、高透光率、高光泽、高韧性(即使在低温环境中)、良好的耐化学品性,也改善了缺点,不易发生应力开裂,良好的涂覆性能,低吸湿率,易脱模。
    PC/PET的特性:
    (1)一般性能 PET树脂为乳白色半透明或无色透明体,相对密度1.38,透光率为90%。PET属于中等阻隔性材料。PET的吸水率为0.6%,吸水性较大。
    (2)力学性能PET膜的拉伸强度很高,可与铝箔婚美,是HDPE膜的9倍,是PC和PA膜的3倍。增强PET的端小、耐疲劳极好(好于增强PC和PA)、耐磨性和耐摩擦性良好。PET的力学性能受温度影响较小。
    (3)热学性能 纯PET 的耐热性能不高,但增强处理后大幅度提高,在180C时的机械性能比PF层压板好,是增强的热塑性工程塑料中耐热较好的品种。PET的耐热老化性好,脆化温度为-70C,在-30C时仍具有一定韧性。PET不易燃烧,火焰呈黄色,有滴落。
    (4)电学性能 PET虽为极性聚合物,但电绝缘性优良,在高频下仍能很好保持PET的耐电晕性较差,不能用于高压绝缘:电绝缘性受温度和湿度影响,并以湿度的影响较大
    PC/PET 的应用:
    有优异的性能,被广泛的用于密封材料、滑动材料、防腐材料、绝缘材料及医用材料等。具体有:
    (1)耐腐蚀方面用纯F4树脂制造各种化工容器和零件,如管材、储罐、反应釜、设备衬里、阀门、泵体、接头、过滤材料、分离材料等一切与有腐蚀性介质接触的制品。
    (2)耐磨方面对F4进行填充耐磨改性处理,可用于耐磨材料,如转动、静密封环、活塞环、垫圈、阀瓣、阀座、轴承、轴瓦、滑块、导轨等
    (3)绝缘材料用纯F4树脂制造耐高温、高频电绝缘制品,如高频绝缘子、高频电缆、耐潮湿电缆、电容器线圈、电机槽的绝缘及集成电路板等。
    沙伯基础PC/PET型号介绍:
    XYLEXMRESINSHX7509HP
    XYLEXM RESINSHX8300HP
    XYLEXM RESINSX7300
    XYLEXM RESINSX7300CLX7607XYLEXD RESINS
    XYLEXmRESINSX7519HP
    XYLEXNRESINSX8210
    XYLEXM RESINSX8300
    XYLEXM RESINSX84109ACXYLEXMRESINS
    X8519

  • 留言

    *详细需求:
    *手  机:
    联 系 人:
    电    话:
    E-mail:
    公  司:
    谷瀑服务条款》《隐私政策
东莞市领汉时代新材料有限公司 电话:0769-87781190 手机:13929209907 地址: 东莞市樟木头南方商业大楼312室
内容声明:谷瀑为第三方平台及互联网信息服务提供者,谷瀑(含网站、客户端等)所展示的商品/服务的标题、价格、详情等信息内容系由店铺经营者发布,其真实性、准确性和合法性均由店铺经营者负责。谷瀑提醒您购买商品/服务前注意谨慎核实,如您对商品/服务的标题、价格、详情等任何信息有任何疑问的,请在购买前通过谷瀑与店铺经营者沟通确认;谷瀑上存在海量店铺,如您发现店铺内有任何违法/侵权信息,请在谷瀑首页底栏投诉通道进行投诉。