德国TOPASCOC 8007F-04 光学级耐高温抗化学防潮包装薄膜

详细信息

	品牌：德国TOPAS		加工级别：注塑级		用途级别：医疗级
	类型：标准料

TOPAS® 8007F-04

Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.

Selected Applications

Pharmaceutical blisters

Deep draw barrier trays

Shrink films and labels

Twist films

Decorative sheet

Food packaging

Healthcare and food contact

Leading Attributes

Clarity, forming, barrier, purity, halogen-free

Excellent deep forming, unlike other barriers

High shrink, low stress, gloss, clarity, toughness

High gloss, outstanding deadfold, clean cutting

Gloss, hardness, chemical resistance, forming

Not manufactured with BPA, phthalates, or halogens

Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

TOPAS 8007F-400 - robust extrusion grade especially for PE blends

TOPAS 8007F-600 - robust clarity extrusion grade especially for PE blends

物性信息：

基本信息
特性	纯度高防潮刚性，高高光共聚物耐化学性良好清晰度，高韧性良好食品接触的合规性通用无 BPA 无定形的无卤
用途	包装薄膜标签流延薄膜片材食品包装通用药品包装医疗/护理用品
机构评级	DMF 12132 FDA FCN 405 欧洲 10/1/2011 12:00:00 AM
形式	粒子
加工方法	薄膜挤出吹塑薄膜共挤薄膜流延薄膜热成型

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm³	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	1.8	g/10 min	ISO 1133
230°C/2.16 kg	11	g/10 min	ISO 1133
溶化体积流率（MVR）			ISO 1133
190°C/2.16 kg	2.00	cm³/10min	ISO 1133
230°C/2.16 kg	12.0	cm³/10min	ISO 1133
吸水率 (饱和, 23°C)	0.010	%	ISO 62

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	70	µm
拉伸模量			ISO 527-3/1
MD : 70 µm, 铸造薄膜	2200	MPa	ISO 527-3/1
TD : 70 µm, 铸造薄膜	1800	MPa	ISO 527-3/1
拉伸应力			ISO 527-3/50
MD : 断裂, 70 µm, 铸造薄膜	57.0	MPa	ISO 527-3/50
TD : 断裂, 70 µm, 铸造薄膜	50.0	MPa	ISO 527-3/50
伸长率			ISO 527-3/50
MD : 断裂, 70 µm, 铸造薄膜	2.9	%	ISO 527-3/50
TD : 断裂, 70 µm, 铸造薄膜	3.0	%	ISO 527-3/50
落锤冲击 (70 µm, 铸造薄膜)	< 36	g	ISO 7765-1
埃尔曼多夫抗撕强度			ISO 6383-2
MD : 70 µm, 铸造薄膜	2.2	N	ISO 6383-2
TD : 70 µm, 铸造薄膜	2.3	N	ISO 6383-2
透氧率 (23°C, 70 µm, 挤塑薄膜, 50% RH)	25	cm³·mm/m²/atm/24 hr	ASTM D3985
水气透过率 (70 µm, 23°C, Cast Film, 85% RH)	0.094	g·mm/m²/atm/24 hr	ASTM F1249

热性能	额定值	单位制	测试方法
玻璃转化温度	78.0	°C	ISO 11357-2

光学性能	额定值	单位制	测试方法
光泽度 (60°, 70.0 µm, 铸造薄膜)	> 100		ISO 2813
雾度 (70.0 µm, 铸造薄膜)	< 1.0	%	ISO 14782

挤出	额定值	单位制
挤塑机进料部分	20 到 60	°C
挤出机螺杆长径比L / D	> 28:1
料筒1区温度	210 到 220	°C
料筒2区温度	230 到 240	°C
料筒3区温度	230 到 240	°C
料筒4区温度	230 到 240	°C
口模温度	230 到 240	°C

挤压说明
Head pressure: P > 140 bar / 2000 psi; Fine screen packs as neededScrew speed: RPM > 50% nominalScrew design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 inch Grooved Feed: Hot temperature: 120°C (248°F)

留言

*详细需求：	德国TOPASCOC 8007F-04 光学级耐高温抗化学防潮包装薄膜
*手机：
联系人：
电话：
E-mail：
公司：
	已经阅读并同意《谷瀑服务条款》《隐私政策》允许谷瀑将询价单分发给更多优质供应商

供应商的其他相关信息
查看更多
美国杜邦 TPEE 4056 抗

美国杜邦 TPEE 6356 高

美国杜邦 TPEE 6356 高

美国杜邦TPEE 4556 抗

美国杜邦TPEE 8238 耐

产品搜索
产品分类
留言

文国祥

在线联系

手机：13929209907

您输入的内容请介于 5 到 2000 字之间

请输入正确手机号

同意《谷瀑服务条款》《隐私政策》

允许谷瀑将询价单分发给更多优质供应商
公司相册

东莞市领汉时代新材料有限公司

东莞市领汉时代新材料有限公司主要经营：PA12.PEI.PPS.PA66,,PC,无卤阻燃.耐寒PC,阻燃ABS,HTN高温尼龙.导热塑料 耐磨塑料 基础创新特殊塑料。

德国TOPASCOC 8007F-04 光学级 耐高温 抗化学 防潮 包装薄膜

店内推荐产品

详细信息

TOPAS® 8007F-04

留言

供应商的其他相关信息

产品搜索

产品分类

留 言

公司相册

东莞市领汉时代新材料有限公司主要经营：PA12.PEI.PPS.PA66,,PC,无卤阻燃.耐寒PC,阻燃ABS,HTN高温尼龙.导热塑料耐磨塑料基础创新特殊塑料。

德国TOPASCOC 8007F-04 光学级耐高温抗化学防潮包装薄膜

留言