Chemours 340 PFA Perfluoroalkoxy Copolymer

PFA
Chemours
产品说明：
Combines the processing ease of conventional thermoplastic resins with the excellent properties of PTFE. High chemical resistance, superior electrical properties, high service temperatures, superior high temperature creep resistance, excellent low temperature toughness, and exceptional flame resistance. Processed by conventional melt-extrusion and molding techniques. Resin Characteristics: General purpose; highest flow rate. Uses: Tubing; injection- or blow-molded articles

Chemours was formed from former DuPont performance chemicals businesses, including DuPont Fluoroproducts, in 2015. This specific product was discontinued prior to the formation of Chemours.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	2.12 - 2.17 g/cc	2.12 - 2.17 g/cc	ASTM D792
吸水率	<= 0.030 %	<= 0.030 %	24 hours; ASTM D570
熔体流动速率	14 g/10 min	14 g/10 min	ASTM D3307

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)	55	55	ASTM D2240
极限抗拉强度	25.0 MPa	3630 psi	ASTM D3307
	12.0 MPa @Temperature 250 °C	1740 psi @Temperature 482 °F	ASTM D3307
	129 MPa @Temperature -196 °C	18700 psi @Temperature -321 °F	ASTM D1780
抗张强度(屈服)	13.8 MPa	2000 psi	ASTM D3307
伸长率 (断裂)	300 %	300 %	ASTM D3307
	8.0 % @Temperature -196 °C	8.0 % @Temperature -321 °F	ASTM D1708
	480 % @Temperature 250 °C	480 % @Temperature 482 °F	ASTM D3307
弯曲模量	0.590 GPa	85.6 ksi	ASTM D790
	0.0550 GPa @Temperature 250 °C	7.98 ksi @Temperature 482 °F	ASTM D790
抗压强度	24.0 MPa @Temperature 23.0 °C	3480 psi @Temperature 73.4 °F	ASTM D695
	414 MPa @Temperature -196 °C	60000 psi @Temperature -321 °F	ASTM D695
Compressive Modulus	69.0 GPa @Temperature 23.0 °C	10000 ksi @Temperature 73.4 °F	ASTM D695
	4690 GPa @Temperature -196 °C	680000 ksi @Temperature -321 °F	ASTM D695
悬壁梁缺口冲击强度	NB	NB	ASTM D256
	0.640 J/cm @Temperature -196 °C	1.20 ft-lb/in @Temperature -321 °F	ASTM D256-72a
动态摩擦系数	0.21	0.21	3 ft/min; 100 psi; dry vs. steel
	0.214	0.214	10 ft/min; 100 psi; dry vs. steel
	0.229	0.229	30 ft/min; 100 psi; dry vs. steel
	0.289	0.289	50 ft/min; 100 psi; dry vs. steel
K (wear) Factor	1400 x 10-8 mm³/N-M	694 x 10-10 in³-min/ft-lb-hr	50 ft/min; 100 psi; dry vs. steel
	1980 x 10-8 mm³/N-M	983 x 10-10 in³-min/ft-lb-hr	30 ft/min; 100 psi; dry vs. steel
	3205 x 10-8 mm³/N-M	1591 x 10-10 in³-min/ft-lb-hr	3 ft/min; 100 psi; dry vs. steel
	3700 x 10-8 mm³/N-M	1837 x 10-10 in³-min/ft-lb-hr	10 ft/min; 100 psi; dry vs. steel

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	1.00e+18 ohm-cm	1.00e+18 ohm-cm	ASTM D257
表面电阻率	>= 1.00e+17 ohm	>= 1.00e+17 ohm	ASTM D257
介电常数	2.03 @Frequency 60.0 - 1.00e+6 Hz	2.03 @Frequency 60.0 - 1.00e+6 Hz	ASTM D150
介电强度	80.0 kV/mm @Thickness 0.0250 mm	2030 kV/in @Thickness 0.000984 in	Short time; ASTM D149
耗散因数	0.00010 @Frequency 60.0 - 1.00e+6 Hz	0.00010 @Frequency 60.0 - 1.00e+6 Hz	ASTM D150
耐电弧性	>= 180 sec	>= 180 sec	ASTM D495

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	140 µm/m-°C @Temperature 21.0 - 100 °C	77.8 µin/in-°F @Temperature 69.8 - 212 °F	ASTM D696
	170 µm/m-°C @Temperature 100 - 149 °C	94.4 µin/in-°F @Temperature 212 - 300 °F	ASTM D696
	210 µm/m-°C @Temperature 149 - 208 °C	117 µin/in-°F @Temperature 300 - 406 °F	ASTM D696
比热容	1.172 J/g-°C @Temperature 100 °C	0.2801 BTU/lb-°F @Temperature 212 °F
熔融温度	302 - 310 °C	576 - 590 °F	ASTM D3418
*高工作温度, Air	260 °C	500 °F
玻璃化转变温度，Tg	-80.0 °C	-112 °F	Glass II
	90.0 °C	194 °F	Glass I
可燃性(UL94)	V-0	V-0
极限氧指数	>= 95 %	>= 95 %	ASTM D2863

光学性能	额定值 (公制)	额定值 (英制)	测试方法
折射率	1.35	1.35	ASTM D542-50
雾度	4.0 %	4.0 %	ASTM D1003-52
Transmission, Visible	91 - 96 % @Thickness 0.0250 mm	91 - 96 % @Thickness 0.000984 in	0.40 to 0.70 µm
IR Transmittance	96 - 98 %	96 - 98 %	0.025; 0.70 to 2.40 µm
UV Transmittance	77 - 91 % @Thickness 0.0250 mm	77 - 91 % @Thickness 0.000984 in	0.25 to 0.70 µm

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	379 - 399 °C	714 - 750 °F	Cure Temperature

材料描述		测试方法
20% Hydrochloric Acid Transmission, g/100sq in.	<0.02
50% Sodium Hydroxide Transmission, g/100sq in.	<.02
Acetic Acid Transmission, g/100sq in.	0.41
Acetone Transmission, g/100sq in.	0.95
Acetophenone Transmission, g/100sq in.	0.5
Benzene Transmission, g/100sq in.	0.64
Carbon Tetrachloride Transmission, g/100sq in.	0.31
Chemical/Solvent Resistance	Excellent
Ethyl Acetate Transmission, g/100sq in.	0.76
Folding Endurance, # cycles, .18-.20 mm	15000
Heat of Combustion J/g	5300	ASTM D240
Hexane Transmission, g/100sq in.	0.56
Piperidine Transmission, g/100sq in.	0.04
Red Fuming Nitric Acid Transmission, g/100sq in.	7.5-1.4
Salt Spray Resistance on aluminum, Hours	1000
Sulfuric Acid Transmission, g/100sq in.	0.00001
Water Transmission, g/100sq in.	0.4
Weather Resistance	10	Years unaffected in Florida Exposure

1、 为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强，溶体粘度下降，而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型方法加工成制品。
2、长期使用温度-196--260摄氏度，有卓越的耐化学腐蚀性，对所有化学品都耐腐蚀，摩擦系数在塑料中*低，还有很好的电性能，其电绝缘性不受温度影响，有“塑料王”之称。
3、其耐化学药品性与聚四氟乙烯相似，比偏氟乙烯好。
4、其抗蠕变性和压缩强度均比聚四氟乙烯好，拉伸强度高，伸长率可达100-300%。介电性好，耐辐射性能优异。阻燃性达V0级。
5、适于制作耐腐蚀件，减磨耐磨件、密封件、绝缘件零件。
6、高温电线、电缆绝缘层，防腐设备、密封材料、泵阀衬套，和化学容器。
成型性能
1.结晶料,吸湿小。可采用通常得热塑性塑料得加工方法加工成制品。
2.流动性差，极易分解，分解时产生腐蚀气体。宜严格控制成型温度不要超过475摄氏度，模具应加热至150-200摄氏度，浇注系统对料流阻力应小。
3.半透明粒料，注塑、挤出成型。成型温度350-400摄氏度，475摄氏度以上容易引起变色或发生气泡。并注意脱模会较困难。
4、因熔融的材料对金属有腐蚀作用，长期生产，模具需要电镀铬处理。
全氟烷氧基树脂
PFA树脂相对来说是比较新的可熔融加工的氟塑料。
PFA的熔点大约为580F，密度为2.13— 2.16g/cc（克/立方厘米）。PFA与 PTFE和FEP相似，但在302T以上时，机械性能略优于FEP，且可在高达500F下的温度下使用，它的耐化学品性与PTFE相当。PFA的产品形式有用于模塑和挤塑的粒状产品，用于旋转模塑和涂料的粉状产品；其半成品有膜、板、棒和管材。美国市场经销的PFA树脂有DUPOut公司的Teflon牌、Daikin公司的Neoflon牌、Ansimont公司的Hthen牌、HOechst Celanese公司的 Hostafl牌。PFA的用途与FEP类似。