Plexiglas® Resist zk4BR

Polymethyl Methacrylate Acrylic
Evonik Industries AG
产品说明：
Product Profile:
PLEXIGLAS® Resist zk4BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified
PLEXIGLAS® molding compounds are

• excellent weather resistance

• excellent transmission and clarity

• brilliant appearance

• the pleasant feel and sound of the moldings

PLEXIGLAS® Resist zk4BR is characterized by the following special properties:

• high break resistance and impact strength

• improved resistance to stress cracking

• balanced property profile

• AMECA listing.

Application:
Used for extruding and coextruding sheets and
profiles as well as for injection molding

Examples:
extruded and injection-molded luminaire, covers, extruded hollow profiles, writing, utensils such as stencils and fountain pens, ppliance housings, coextruded profiles for window frames, gutters, downspouts, and housewares such as cutlery handles, bowls, cookie jars.
物性信息：

基本信息
黄卡编号	E65495-247816
添加剂	冲击改性剂
特性	冲击改性 高 ESCR（抗应力开裂） 抗撞击性，高 耐气候影响性能良好 清晰度，高 外观良好
用途	保护性遮盖物 户外家具 家用货品 室外应用 外壳 文具 型材
形式	粒子
加工方法	共挤出成型 挤出 注射成型
多点数据	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

物理性能	额定值	单位制	测试方法
密度	1.18	g/cm³	ISO 1183
溶化体积流率（MVR） (230°C/3.8 kg)	4.50	cm³/10min	ISO 1133
吸水率			ISO 62
23°C, 24 hr	2.0	%	ISO 62
平衡, 23°C, 50% RH	0.60	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	2800	MPa	ISO 527-2/1
拉伸应力 (屈服)	71.0	MPa	ISO 527-2/50
拉伸应变 (屈服)	4.5	%	ISO 527-2/50
标称拉伸断裂应变	19	%	ISO 527-2

冲击性能	额定值	单位制	测试方法
简支梁无缺口冲击强度 (23°C)	25	kJ/m²	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa, 未退火	99.0	°C	ISO 75-2/B
1.8 MPa, 未退火	95.0	°C	ISO 75-2/A
玻璃转化温度	108	°C	ISO 11357-2
维卡软化温度	102	°C	ISO 306/B50
线形热膨胀系数 - 流动 (0 到 50°C)	8.0E-5	cm/cm/°C	ISO 11359-2

可燃性	额定值		测试方法
UL 阻燃等级 (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

光学性能	额定值	单位制	测试方法
折射率	1.490		ISO 489
透射率 1	92.0	%	ISO 13468-2
雾度	< 1.5	%	ASTM D1003

注射	额定值	单位制
干燥温度	< 90.0	°C
干燥时间	2.0 到 3.0	hr
加工（熔体）温度	220 到 260	°C
模具温度	50.0 到 70.0	°C

备注
1 .	D65

LED灯系列

美国阿莫科PPA A-4422 LS WH 118 做LED灯支架料

美国阿莫科PPA A-4122 HR WH 117 LED灯灯架料

美国阿莫科PPA A-1133 NL WH 886 LED灯架料

日本三菱PC EFD8000 防火V0,透光率85%左右光扩散半透明PC LED灯泡

日本三菱PC EFD2110U 防火V0,透光率85%左右光扩散半透明PC LED灯管

日本三菱PC EFD2140VUR 防火V2,透光率66%左右光扩散半透明PC LED灯管

日本三菱PC EFD2230U 防火V0,透光率67%左右光扩散半透明PC LED灯管

红外线穿透PC德国拜耳 3103GEF-75 红外线穿透

红外线穿透PC德国拜耳 2405 450601 红外线穿透

基础创新塑料PC DMX9455 光扩散磨砂级遮光 LED灯泡

基础创新塑料PC DMX2415 磨砂级 防刮伤

PMMA法国阿科玛 V045 光扩散 磨砂级 LED灯泡

德固赛PMMA 8NDF20 8NDF21 磨砂级 LED灯泡

德固赛PMMA 8NDF22 8NDF23 磨砂级 LED灯泡

PC EXL9330,EXL9112R 防火V0 超韧耐寒 EXL1414

PC LS2,LS3 光学级 汽车灯专用料

PC 1239,PK2870 食品级，包装用料

PC DL-4020,DL-4030 铁氟龙合金，低磨耗高韧性 高抗冲 抗疲劳

PC DMX9455 光扩散磨砂级遮光伤 LED灯泡PC DMX2415 磨砂级 防刮花

汽车轻量化材料

 

新能源汽车补贴新增落地，提高续航里程是车企目前面临的一大重要挑战，而汽车轻量化技术是有效提高续航里程的方法之一。汽车自重每减少10%，其能源消耗可降低6%~8%，同时尾气排放量可降低4%左右，因此汽车轻量化技术是实现汽车节能、环保、安全等发展目标的重要新技术。

汽车轻量化的关键是使用轻质、安全、高性能的材料，塑料及其复合材料、弹性体、碳纤维复合材料等在实现汽车减重的目标中都起到了重要的作用。其中 PMMA 凭借光学性能优良、重要轻、耐候性好等优点被广泛应用于车身多个位置，是 PMMA 应用逐步起步的重要领域。

车灯：车灯起到照明和信号的作用，要求材料具有良好的透光性、耐冲击和耐老化性。PMMA 因具有质轻、易着色、美观等优点而广泛应用于新能源汽车车尾灯灯罩。

车窗玻璃：车窗占汽车整体比重较大，因此使用低密度、质量轻的材料作为车窗是驱车减重的重要手段。汽车车窗对透光、抗冲击、耐候和碎片少等要求较高，PMMA 在满足上述条件的同时，还具备抗紫外线辐射、抗老化风化的作用，因此已经被欧洲大部分汽车制造商用作汽车侧边及后边挡风玻璃材料，较传统玻璃，重量可以减轻 40%～50%。

仪表盘：PMMA韧性非常好，韧性*好，冲击强度很高，抗震动不开裂，过耐压测试不开裂，强度很好，光学透明度好，用作仪表盘不会开裂。

保险杠：PMMA和ABS复合材料可用作新能源汽车保险杠，集合了 PMMA 抗划伤、不易褪色、环保及 ABS 抗冲击、耐温性好、电气性佳、易喷镀等优点，同时较镁铝合金成本更低。

 

PMMA未来发展趋势分析

PMMA不仅拥有良好的机械强度、一定的化学稳定性，而且还具有优异的光学透光性，能够广泛应用于各领域。当前聚甲基丙烯酸甲酯的合成方向主要致力于提高其耐热性和加工流动性，优化PMMA工艺路线，使其耐热性和加工流动性得以有效提高，保障产品性能及成本优势，满足市场要求。

未来，高精尖端PMMA产品市场潜力需求量会越来越大，研究也将从PMMA的改性入手。总之，随着科技的进步，PMMA的应用领域会越来越广，因此对其合成方向及应用领域的深入开发和研究还是十分有价值的。