Chemours Teflon® PTFE Grade 7B Granular Compression Molding Resin

PTFE
Chemours
产品说明：
DuPont™ Teflon® PTFE 7B is a white granulated powder with an ultra fine particle size and high bulk density. The ultra-fine particle size minimizes voids even at relatively low molding pressure. Teflon® PTFE 7B is an excellent choice for moldings requiring optimum mechanical and electrical properties. The ultra-fine particle size of Teflon® PTFE 7B promotes good capture and uniform distribution of inorganic fillers when they are added to modify the mechanical properties of moldings. Teflon® PTFE 7B exhibits a mold shrinkage that is intermediate of the mold shrinkage of 7A and 7C grades.
DuPont™ Teflon® PTFE 7B 是一种白色颗粒状粉末，具有超细粒径和高堆积密度。即使在相对较低的成型压力下，超细颗粒尺寸也能*大限度地减少空隙。Teflon® PTFE 7B 是需要*佳机械和电气性能的模制品的绝佳选择。当添加无机填料来改变模制品的机械性能时，Teflon® PTFE 7B 的超细粒度可促进无机填料的良好捕获和均匀分布。Teflon® PTFE 7B 的成型收缩率介于 7A 和 7C 等级的成型收缩率之间。

Properly processed products made from neat Teflon® PTFE 7B provide the superior properties typical of the fluoropolymer resins: retention of properties after service at 260°C (500°F), useful properties at –240°C (–400°F), chemical inertness to nearly all industrial chemicals and solvents, and low friction and antistick surfaces. Dielectric properties are outstanding and stable with frequency and temperature. Molded products have moderate stiffness and high ultimate elongation. In a flame situation, products of Teflon® PTFE 7B resist ignition and do not themselves promote flame spread. When ignited by flame from other sources, their contribution of heat is small and with very little smoke.

由纯 Teflon® PTFE 7B 制成的经过正确加工的产品可提供含氟聚合物树脂典型的卓越性能：在 260°C (500°F) 下使用后仍保留性能，在 –240°C (–400°F) 下保持有用性能，化学性能对几乎所有工业化学品和溶剂都呈惰性，并且具有低摩擦和防粘表面。介电性能出色且随频率和温度稳定。成型品具有适中的刚度和较高的极限伸长率。在火焰情况下，Teflon® PTFE 7B 产品能够抵抗点燃，并且本身不会促进火焰蔓延。当被其他来源的火焰点燃时，它们贡献的热量很小，并且产生的烟雾也很少。

Statements, or data, regarding behavior in a flame situation are not intended to reflect hazards presented by this or any other material when under actual fire conditions.

有关火焰情况下的行为的声明或数据并不旨在反映该材料或任何其他材料在实际火灾条件下所带来的危险。

Applications

Many end products are molded or fabricated from moldings of Teflon® PTFE 7B—or made with filled compounds based on Teflon® PTFE 7B. The filled compounds provide a wide choice of modified mechanical properties. End products using Teflon® PTFE 7B include skived film and sheet, gaskets, bridge or pipeline bearing pads, piston rings, and diaphragms.

Chemours was formed from former DuPont performance chemicals businesses, including DuPont Fluoroproducts, in 2015.

许多*终产品都是由 Teflon® PTFE 7B 模制品模制或制造而成，或者由基于 Teflon® PTFE 7B 的填充化合物制成。填充化合物提供了多种改进的机械性能选择。使用 Teflon® PTFE 7B 的*终产品包括车削薄膜和片材、垫圈、桥梁或管道轴承垫、活塞环和隔膜。科慕于 2015 年由杜邦氟产品等前杜邦高性能化学品业务部门组建而成。

物性信息：

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	2.16 g/cc	2.16 g/cc	ASTM D4894
体积密度	0.330 g/cc	0.0119 lb/in³	ASTM D4894
吸水率	<= 0.010 %	<= 0.010 %	24 hours; ASTM D570
粒径	24 µm	24 µm	ASTM D4894
线性成型收缩率	0.044 cm/cm	0.044 in/in	at preform pressure of 35 Mpa; ASTM D4894

机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	58	58	ASTM D785
肖氏硬度 (邵氏 A)	98	98	ASTM D2240
肖氏硬度 (邵氏 D)	50 - 65	50 - 65	ASTM D2240
极限抗拉强度	36.5 MPa	5290 psi	ASTM D4894
伸长率 (断裂)	400 %	400 %	ASTM D4894
弯曲模量	0.496 GPa	71.9 ksi	ASTM D790
泊松比	0.46	0.46	approaches a limit of 0.50 at higher temperature
悬壁梁缺口冲击强度	1.89 J/cm	3.54 ft-lb/in	ASTM D256
摩擦系数	0.050 - 0.10	0.050 - 0.10	ASTM D 1894
动态摩擦系数	0.10	0.10	V = 10 fpm; P= 800 - 1000 psi
	0.13	0.13	V = 100 fpm; P= 80 - 100 psi
静态摩擦系数	0.050 - 0.080	0.050 - 0.080	500 psi
K (wear) Factor	5040 x 10-8 mm³/N-M	2500 x 10-10 in³-min/ft-lb-hr	unlubricated vs. soft carbon steel
Limiting Pressure Velocity	0.0420 MPa-m/sec @Temperature 21.0 - 27.0 °C	1200 psi-ft/min @Temperature 69.8 - 80.6 °F	at 10 fpm
	0.0631 MPa-m/sec @Temperature 21.0 - 27.0 °C	1800 psi-ft/min @Temperature 69.8 - 80.6 °F	at 100 fpm
	0.0876 MPa-m/sec @Temperature 21.0 - 27.0 °C	2500 psi-ft/min @Temperature 69.8 - 80.6 °F	at 1000 fpm
泰伯磨损，毫克/1000次	8.9	8.9	1000 cycles; CS-17F wheel

电气性能	额定值 (公制)	额定值 (英制)	测试方法
体积电阻率	>= 1.00e+18 ohm-cm	>= 1.00e+18 ohm-cm	ASTM D257
表面电阻率	>= 1.00e+18 ohm	>= 1.00e+18 ohm	ASTM D257
介电常数	2.1 @Frequency 1e+6 Hz	2.1 @Frequency 1e+6 Hz	ASTM D150
介电强度	18.0 kV/mm	457 kV/in	100 micrometers film; ASTM D149
耗散因数	<= 0.00010 @Frequency 1e+6 Hz	<= 0.00010 @Frequency 1e+6 Hz	ASTM D150
耐电弧性	>= 300 sec	>= 300 sec	ASTM D495

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	112 µm/m-°C @Temperature -100 - 25.0 °C	62.2 µin/in-°F @Temperature -148 - 77.0 °F
	124 µm/m-°C @Temperature 25.0 - 100 °C	68.9 µin/in-°F @Temperature 77.0 - 212 °F
	220 µm/m-°C @Temperature 25.0 - 300 °C	122 µin/in-°F @Temperature 77.0 - 572 °F
	790 µm/m-°C @Temperature 20.0 - 25.0 °C	439 µin/in-°F @Temperature 68.0 - 77.0 °F	Large volume change in the 18-25°C transition range
比热容	1.20 J/g-°C @Temperature 40.0 °C	0.287 BTU/lb-°F @Temperature 104 °F
	1.30 J/g-°C @Temperature 150 °C	0.311 BTU/lb-°F @Temperature 302 °F
	1.40 J/g-°C @Temperature 20.0 °C	0.335 BTU/lb-°F @Temperature 68.0 °F
	1.50 J/g-°C @Temperature 260 °C	0.359 BTU/lb-°F @Temperature 500 °F
导热系数	0.250 W/m-K	1.74 BTU-in/hr-ft²-°F
	0.300 W/m-K @Temperature 20.0 - 260 °C	2.08 BTU-in/hr-ft²-°F @Temperature 68.0 - 500 °F
熔融温度	317 - 337 °C	603 - 639 °F	ASTM D4894
*高工作温度, Air	260 °C	500 °F	retains useful mechanical properties
*低工作温度, Air	-268 °C	-450 °F	retains useful mechanical properties
	-79.0 °C	-110 °F	remains highly flexible
可燃性(UL94)	V-0	V-0
极限氧指数	>= 95 %	>= 95 %	ASTM D2863

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工温度	379 - 429 °C	714 - 804 °F	Cure Temperature

材料描述		测试方法
20% Hydrochloric Acid Transmission, g/100sq in.	<0.01
50% Sodium Hydroxide Transmission, g/100sq in.	<.01
Acetic Acid Transmission, g/100sq in.	0.41
Acetone Transmission, g/100sq in.	0.95
Acetophenone Transmission, g/100sq in.	0.5
Benzene Transmission, g/100sq in.	0.64
Carbon Tetrachloride Transmission, g/100sq in.	0.31
Chemical/Solvent Resistance	Excellent
Detergent Resist. on grit-blasted aluminum, Hours	624
Detergent Resistance on aluminum, Hours	264
Detergent Resistance on grit-blasted steel, Hours	24
Ethyl Acetate Transmission, g/100sq in.	0.76
Folding Endurance, # cycles, .18-.20 mm	>10^6
Heat of Combustion J/g	5100	ASTM D240
Hexane Transmission, g/100sq in.	0.56
Piperidine Transmission, g/100sq in.	0.04
Red Fuming Nitric Acid Transmission, g/100sq in.	7.5-1.4
Salt Spray Resistance on aluminum, Hours	>744
Salt Spray Resistance on steel, Hours	192
Sulfuric Acid Transmission, g/100sq in.	0.00001
Water Transmission, g/100sq in.	0.4
Weather Resistance	20	Years unaffected in Florida Exposure

1聚四氟乙烯可采用压缩或挤出加工成型:也可制成水分散液，用于涂层、浸渍或制成纤维。
聚四氟乙烯在原子能、国防、航天、电子、电气、化工、机械、仪器、仪表、建筑、纺织、金属表面处理、制药、医疗、纺织、食品、冶金冶炼等工业中广泛用作耐高低温、耐腐蚀材料，绝缘材料，防粘涂层等，，使之成为不可取代的产品。聚四氟乙烯具有杰出的优良综合性能，耐高温，耐腐蚀、不粘、自润滑、优良的介电性能、很低的摩擦系数。用作工程塑料，可制成聚四氟乙烯管、棒、带、板、薄膜等，一般应用于性能要求较高的耐腐蚀的管道、容器、泵、阀以及制雷达、高频通讯器材、无线电器材等。在PTFE中加入任何可以承受PTFE烧结温度的填充剂，机械性能可获得大大的改善，同时保持PTFE其它优良性能。填充的品种有玻璃纤维、金属金属化氧化物、石墨、二硫化、碳纤维、聚酷亚胺、EKONOL···等，耐磨耗、极限PV值可提高1000倍。
特氟龙布聚四氟乙烯管材选用悬浮聚合聚四氟乙烯树脂经柱塞挤压加工制成。在已知塑料中聚四氟乙烯具有特好的耐化学腐蚀性能及介电性能。聚四氟乙烯编织盘根是种良好的动密封材料，是由膨体聚四氯乙烯带条编织而成，具有低摩擦系数、耐磨耐化学腐蚀、密封性良好、不水解、不变硬等优良性能。用于各种介质中工作的衬垫密封件和润滑材料，以及在各种频率下使用的电绝缘件、电容器介质、导线绝缘电器仪表绝缘等。聚四氟乙烯 薄膜适用于作电容器介质、 特种电缆的绝缘层、导线绝缘、电器仪表绝缘及密封衬垫，还可做不粘带、密封带、脱模、密封圈等。 此外，生活中用的不粘锅的内衬也使用聚四氟乙烯制作的，就是利用了聚四氟乙烯耐高温，不粘的特点。
1.可用于棒、管、板、电缆料、生料带等材料的制作，经二次加工还可制成薄板、薄膜及各种异型制品，还可用作润滑剂、稠化剂。
2.可作为塑料、橡胶、涂料、油墨、润滑油、润滑脂等的添加剂。3.可推压成型制成薄壁管、细棒材、异型棒材、电线电缆绝缘层、滚压成薄带作管道丝扣密封材料。
4.用于机械、电子、化工等工业，用于喷涂、浸渍等.
5.用于制浸渍涂料。
6.可制成棒、板、管材、薄膜及各种异型制品，用于航天、化工、电子、机械、医药等领域。
7.可制成高绝缘性电器零件、耐高频电线电缆包皮、耐腐蚀化学器皿、耐高寒输油管、人工器官等。
8.用于电池、纤维布等。
9.可制薄膜、管板棒、轴承、垫圈、阀门及化工管道、管件、设备容器衬里等，用
于电器、化工航空、机械等领域。10.主要用于电气工业，在航天、航空、电子、仪表、计算机等工业中用作电源和信
号线的绝缘层、耐腐、耐磨材料。11.代替石英玻璃器皿应用于原子能、医学、半导体等行业的超纯化学分析和贮存各种酸、碱、有机溶剂。